The clarity of Somos 11122 is ideal when creating lenses, windows, bottles, or, any product that you would like to view the internal components of (with an added clear coat).
Clarity is not the only advantage of this SL material; it has good overall properties, which make Somos 11122 ideal for general prototyping or water flow testing.
These SL parts can be sanded, primed, painted, used as pattern masters for urethane casting, or as final presentation pieces. You may also create QuickCast™ patterns for investment casting.
|Tensile Strength||ASTM D638||47.1 - 53.6 MPa||6,831-7,774 PSI|
|Tensile Modulus||ASTM D638||2,040-2,370 MPa||260,000-287,000 PSI|
|Elongation at Break (%)||ASTM D638||11 - 20%||11 - 20%|
|Flexural Strength||ASTM D790||87 - 101 MPa||9,152-10,756 PSI|
|Flexural Modulus||ASTM D790||2,700-3,000 MPa||296,000-344,000 PSI|
|Impact Strength (notched)||ASTM D256||.2 - .3 J/m||.4 - .6 ft-lb/in|
|Heat Deflection Temp.||ASTM D648||@.46 MPa: 45-54.5°C||@66 PSI: 115-130°F|
|Heat Deflection Temp.||ASTM D648firstname.lastname@example.org MPa: 49-49.7°C||@264 PSI: 120°F|
|Glass Transition Temp.||-||n/a||n/a|
|Hardness||Shore D||D 70 - 74||D 70 - 74|
All values were taken from the documentation supplied by the manufacturer of this particular material. C.ideas inc. makes no claims to the accuracy of this data, as each individual application may vary. Please contact the manufacturer for any questions relating to specific MSDS information.
- Translucent (Standard finish is frosted, clear coat or polished is available)