Accura Xtreme White 200 is a tough, high performance resin. It's white appearance and durability compares well with engineering plastics.
Accura Xtreme White 200, has an extremely high impact resistance, which makes it ideal for functional testing. Xtreme White produces accurate, crisp and clean detail, which is perfect for prototypes, fit, form or presentation models.
These SL parts can be sanded, primed, painted and used as final show pieces. This durable material also works well when creating snap fits or assemblies that require tougher than normal loads.
Although it's extremely durable for testing, it's also the easiest SL material to sand prime and paint. Due to its thicker viscosity, it takes longer to build and may command a slightly higher price than general purpose resins.
|Tensile Strength||ASTM D 638||45 - 50 MPa||6530-7250 PSI|
|Tensile Modulus||ASTM D 638||2300-2630MPa||334-381 KSI|
|Elongation at Break||ASTM D 638||7-20%||7-20%|
|Flexural Strength||ASTM D 790||75-79 MPa||10880-11460 PSI|
|Flexural Modulus||ASTM D 790||2350-2550 MPa||341-370 KSI|
|Impact Strength||ASTM D 256||55-60 J/m||1.03 - 1.24 ft-lb/in|
|Heat Deflection||ASTM D 648||@.46 MPa: 47°C||@66 PSI: 117°F|
|Heat Deflection||ASTM D firstname.lastname@example.org MPa: 42°C||@264 PSI: 108°F|
|CTE||ASTM E 831-93||95 (30-50° C)||53 (77-122° F)|
|CTE||ASTM E 831-93||180 (70-100° C)||100 (122 - 212° C)|
|Water Absorption||ASTM D 570-98||0.38%||0.38%|
|Glass Transition (Tg)||DMA, E”||52°C||126°F|
|Hardness||Shore D||D 78-80||D 78-80|
All values were taken from the documentation supplied by the manufacturer of this particular material. C.ideas inc. makes no claims to the accuracy of this data, as each individual application may vary. Please contact the manufacturer for any questions relating to specific MSDS information.