M100 HR/SR is a rigid general purpose, high-res, semi translucent material with a very low ash content.
M100 utilizes the MJM process, it can produce extremely small fine featured parts or assemblies. The SR produces a milky (white hue) & the HR material is a semi-translucent Royal Blue.
Rigid MJM parts have an extremely high resolution layer slice (0.0006"), Parts as small as 0.0125" can be produced with an incredible level of detail. Since the wax support structure is simply melted away, MJM is ideal for creating thin wireframes, trusses, assemblies & conceptual models.
| TECHNICAL PROPERTIES | TEST | METRIC | IMPERIAL |
|
APPEARANCE/COLORS: HR = Royal Blue (Translucent) SR = Milky White (Translucent) |
| Tensile Strength | ASTM D638 | 24 MPa | 3,500 PSI | ||
| Tensile Modulus | ASTM D638 | 775 MPa | 112,000 PSI | ||
| Elongation at Break (%) | ASTM D638 | 15.6% | 15.6% | ||
| Flexural Strength | ASTM D790 | 42 MPa | 6,100 PSI | ||
| Flexural Modulus | ASTM D790 | 110 MPa | 16,000 PSI | ||
| Impact Strength (notched) | ASTM D256 | n/a | n/a | ||
| Heat Deflection Temp. | ASTM D648 | @.45 MPa: 46°C | @66 PSI: 119°F | ||
| Ash Content | - | <0.01% | <0.01% | ||
|
|||||
| All values were taken from the documentation supplied by the manufacturer of this particular material. C.ideas inc. makes no claims to the accuracy of this data, as each individual application may vary. Please contact the manufacturer for any questions relating to specific MSDS information. | |||||
Jewelry
Very Small Assemblies
Wire Frame or Trusses
Spin Casting Masters
Architectural & Dioramas
SR parts look similar to polypropylene
Smooth contour curves
Text and threads show up well
Low ash content (<0.01%)
Great spin casting or jewelry masters